title = "Influence of scale formation on Copper enrichment behaviour in continuously cast slab",
abstract = "Copper enrichment behavior in continuously cast slab induced by scale formation after continuous cooling in H2O vapor atmosphere and consecutively in air has been experimentally investigated by combining with SEM-EDS analysis, for the purpose to examine the effects of initial slab surface temperature and contents of copper and nickel. For Slab 1 with copper content of 0.1 percent, no visible copper enrichment is found at scale-substrate interface irrespective of the various scale microstructures formed at different initial slab surface temperatures. For Slab 2 with higher contents of copper and nickel, copper-rich phase accumulates and stays at scalesubstrate interface under the condition of lower initial slab surface temperature; while Cu-rich phase in the porous scale formed at higher initial slab surface temperature is noted with simultaneous Ni-enrichment appearing in front of the steel-scale interface. Both a porous scale and high nickel content work together to provide pores for copper-rich phase migration away from interface and occlude within the scale layer.",
keywords = "Continuously cast slab, Copper enrichment, Initial slab surface temperature, Nickel content, Scale formation",
author = "Nan Wang and Shan Yu and Xiaoao Li and Jianhua Xin and Guanghao Chen and Min Chen and Cuihuan Huang",
year = "2016",
doi = "10.1002/9781119274742.ch1",
language = "English",
series = "TMS Annual Meeting",
publisher = "Minerals, Metals and Materials Society",
number = "CONFCODENUMBER",
pages = "5--10",
editor = "Antoine Allanore and Laura Bartlett and Cong Wang and Lifeng Zhang and Jonghyun Lee",
booktitle = "TMS Annual Meeting",
address = "United States",
edition = "CONFCODENUMBER",
note = "EPD Congress 2016 - TMS 2016: 145th Annual Meeting and Exhibition ; Conference date: 14-02-2016 Through 18-02-2016",
}